고망간 Twinning Induced Plasticity 강의 인장 특성에 미치는변형률 속도와 온도의 영향
SCOPUS
KCI
- Title
- 고망간 Twinning Induced Plasticity 강의 인장 특성에 미치는변형률 속도와 온도의 영향
- Authors
- 이정훈; 이성학; 신상용
- Date Issued
- 2017-12
- Publisher
- 한국재료학회
- Abstract
- Four types of high Mn TWIP(Twinning Induced Plasticity) steels were fabricated by varying the Mn and Al content, and the tensile properties were measured at various strain rates and temperatures. An examination of the tensile properties at room temperature revealed an increase in strength with increasing strain rate because mobile dislocations interacted rapidly with the dislocations in localized regions, whereas elongation and the number of serrations decreased. The strength decreased with increasing temperature, whereas the elongation increased. A martensitic transformation occurred in the 18Mn, 22Mn and 18Mn1.6Al steels tested at −196 oC due to a decrease in the stacking fault energies with decreasing temperature. An examination of the tensile properties at −196 oC showed that the strength of the non-Al added high Mn TWIP steels was high, whereas the elongation was low because of the martensitic transformation and brittle fracture mode. Although a martensitic transformation did not occur in the 18Mn1.9Al steel, the strength increased with decreasing temperature because many twins formed in the early stages of the tensile test and interacted rapidly with the dislocations.
- URI
- https://oasis.postech.ac.kr/handle/2014.oak/50846
- DOI
- 10.3740/MRSK.2017.27.12.643
- ISSN
- 1225-0562
- Article Type
- Article
- Citation
- Korean Journal of Materials Research, vol. 27, no. 12, page. 643 - 651, 2017-12
- Files in This Item:
-
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.