Optical properties of CdSe quantum dots in silicate glasses

Abstract

CdSe quantum dots (QDs) were precipitated in silicate glasses under various durations and temperatures of heat-treatment. Absorption and photoluminescence (PL) spectra of the QDs showed the quantum confinement effect from CdSe QDs. When the glass was heat-treated for 10 h, estimated average QD sizes increased from 5.2 nm when the glass was heat-treated at 490 degrees C and to 6.9 nm when it was treated at 500 degrees C. When the glass was heat-treated at 480 degrees C, estimated average QD sizes were 4.9 nm after 20 h and 5.3 nm after 30 h. The PL peak position was independent of the excitation wavelengths: this result indicates that the size distribution of CdSe QDs was narrow. (C) 2010 Elsevier B.V. All rights reserved.