The effect of Co addition on the electrical conductivity of Sr- and Mg-doped LaAlO3
SCIE
SCOPUS
- Title
- The effect of Co addition on the electrical conductivity of Sr- and Mg-doped LaAlO3
- Authors
- Park, JY; Choi, GM
- Date Issued
- 2006-12
- Publisher
- SPRINGER
- Abstract
- Co was added to see its effect on the electrical conductivity of Sr- and Mg-doped LaAlO3 (La0.9Sr0.1 Al0.9Mg0.1O3, LSAM). Electrical conductivities of La0.9Sr0.1(Al0.9Mg0.1)(1-) xCoxO3 (LSAMC) for x = 0-0.20 were measured using 2-probe a.c. and 4-probe d.c. method at temperature between 300 and 1300 degrees C in air, and as a function of Po (2) (1-10(-15) atm) at 1200 degrees C. Electrical conductivities in air increased with increasing Co content, while their activation energy decreased. From the impedance spectroscopy analysis, it was found that both the grain and the grain boundary conductivities of LSAMC samples increased rapidly with Co-addition. LSAMC samples were oxygen ion conductors in low Po-2 and mixed conductors in high Po-2 up to x = 0.1 just like LSAM. With Co-doping, p-type conductivities increased, however, ionic conductivities remained nearly constant.
- Keywords
- mixed conductor; electrical conductivity; perovskite; LaAlO3; OXIDE-ION CONDUCTIVITY; PEROVSKITE-TYPE OXIDE; FUEL-CELLS; ELECTROLYTE; CATHODES
- URI
- https://oasis.postech.ac.kr/handle/2014.oak/23606
- DOI
- 10.1007/s10832-006-4266-3
- ISSN
- 1385-3449
- Article Type
- Article
- Citation
- JOURNAL OF ELECTROCERAMICS, vol. 17, no. 39848, page. 787 - 791, 2006-12
- Files in This Item:
- There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.