Mechanical properties and microstructure evolution of the nano WC-Co coatings fabricated by detonation gun spraying with post heat treatment
SCIE
SCOPUS
- Title
- Mechanical properties and microstructure evolution of the nano WC-Co coatings fabricated by detonation gun spraying with post heat treatment
- Authors
- Park, SY; Kim, MC; Park, CG
- Date Issued
- 2007-03-25
- Publisher
- ELSEVIER SCIENCE SA
- Abstract
- Effects of post heat treatment of thermally sprayed nano WC-Co coatings on their mechanical properties were studied. The thermal behavior of WC particles in the coatings was also investigated. WC-Co coatings containing nano carbide particles in the 100-200 nm range were fabricated by detonation gun spraying. Considerable phase decomposition of WC to W2C and amorphous phase was detected, which degrades the mechanical properties of coatings. In order to improve the mechanical properties of the coatings by recovery of dissociated carbide phases, post heat treatment was conducted in an Ar environment in the temperature range of 400-900 degrees C. Microhardness and fracture toughness were measured by Vickers indentation testing and wear resistance was also evaluated by using a scratch tester. Phase evolution and microstructural changes due to post heat treatment were investigated by optical microscopy, X-ray diffractometry and field-emission scanning electron microscopy. After heat treatment in all temperature ranges, microhardness increased. Fracture toughness and wear resistance of coatings were increased by increasing temperature to 800 degrees C but decreased after heat treatment at 900 degrees C. Amorphous phase disappeared and other carbide phases such as W3Co3C and W6Co6C formed during heat treatment above 700 degrees C. The improved properties were elucidated and discussed in terms of microstructural changes and the relationship between mechanical properties and carbide phase was also discussed. (c) 2006 Elsevier B.V. All rights reserved.
- Keywords
- WC-Co; nano structured coating; post heat treatment; WEAR
- URI
- https://oasis.postech.ac.kr/handle/2014.oak/23477
- DOI
- 10.1016/j.msea.2006.02.444
- ISSN
- 0921-5093
- Article Type
- Article
- Citation
- MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, vol. 449, page. 894 - 897, 2007-03-25
- Files in This Item:
- There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.