Anomalous temperature dependence and tension-compression asymmetry of Fe3Al intermetallics - an internal variable approach
SCIE
SCOPUS
- Title
- Anomalous temperature dependence and tension-compression asymmetry of Fe3Al intermetallics - an internal variable approach
- Authors
- Bang, W; Lim, HT; Ha, TK; Chang, YW
- Date Issued
- 2003-10
- Publisher
- PERGAMON-ELSEVIER SCIENCE LTD
- Abstract
- Tension/compression asymmetry in the high-temperature flow and anomalous yield/flow stress of Fe-28 at% Al-5 at% Cr alloy has been investigated. Flow curves were obtained from a series of tensile and compressive load relaxation tests. Constitutive relations at each deformation conditions were formulated using the internal variable theory based on dislocation dynamics. In this study, high-temperature flow stress of selected material was to be safely described as the sum of internal stress and frictional stress. The anomaly and peak temperature of yield strength seem to be controlled by the anomaly of internal stress and the relative portion of internal and frictional stress in total flow stress, respectively. Asymmetric flow stress was observed in analogy with yield strength. In terms of constitutive parameters, critical stress for frictional flow (Sigma(0)) exhibited considerably higher value in compression, which physically postulates increased critical resolved shear stress (CRSS). Considering the crystallography and microstructure, it is presumably due to the. 'extrinsic' effect of non-deviatoric stress tensor, as proposed in other studies. (C) 2003 Elsevier Ltd. All rights reserved.
- Keywords
- plastic asymmetry; anomalous yielding; intermetallics; CRSS; SINGLE-CRYSTALS; DEFORMATION; STRESS; METALS; PLASTICITY; POTASSIUM; BEHAVIOR; FRACTURE; ALLOY; AL
- URI
- https://oasis.postech.ac.kr/handle/2014.oak/18031
- DOI
- 10.1016/J.IMJECSCI.2
- ISSN
- 0020-7403
- Article Type
- Article
- Citation
- INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, vol. 45, no. 10, page. 1661 - 1670, 2003-10
- Files in This Item:
- There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.