High-cycle fatigue characteristics of non-heat-treated steels developed for bolt applications
SCIE
SCOPUS
- Title
- High-cycle fatigue characteristics of non-heat-treated steels developed for bolt applications
- Authors
- Park, SH; Hong, SG; Chun, YS; Lee, YH; Lee, CS
- Date Issued
- 2012-07-30
- Publisher
- ELSEVIER SCIENCE SA
- Abstract
- High-cycle fatigue behavior of non-heat-treated steels for 900 MPa grade bolt applications, developed as substitutes for tempered martensite (TM) steel, was investigated. Four types of non-heat-treated steels with ferrite-pearlite (F-P) and granular bainitic ferrite (GBF) microstructures were developed by combining alloying and air cooling processes. The developed materials exhibited a similar tensile strength (840-890 MPa) as that of TM steel (910 MPa) but their fatigue ratios R-f = (fatigue strength at 10(7) cycles)/(tensile strength) were somewhat different from each other; in the F-P steels R-f was comparable to that of the TM steel but the GBF steels showed a somewhat reduced R-f (similar to 11%), due to a change in the crack initiation mechanism. For both TM and F-P steels, fatigue cracks initiated at the specimen surface, irrespective of the stress amplitude applied, and thus their R-f values became similar and conventional stress amplitude vs. fatigue life (S-N) curves were resulted. In the GBF steels, however, fatigue cracks initiated at inclusions, as the stress amplitude applied was low; this different crack initiation mechanism led to a reduction of fatigue strength and caused a duplex S-N curve. It was found that the F-P steels are a promising candidate to substitute for the TM steel in terms of the tensile strength and high-cycle fatigue resistance. (c) 2012 Elsevier B.V. All rights reserved.
- Keywords
- Non-heat-treated steel; High-cycle fatigue; Duplex S-N curve; Crack initiation mechanism; CARBON BAINITIC STEELS; MICROALLOYED STEELS; FERRITE-PEARLITE; FORGING STEELS; BEHAVIOR; STRENGTH; LIFE; MICROSTRUCTURES; TOUGHNESS; TITANIUM
- URI
- https://oasis.postech.ac.kr/handle/2014.oak/14678
- DOI
- 10.1016/J.MSEA.2012.04.043
- ISSN
- 0921-5093
- Article Type
- Article
- Citation
- MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, vol. 550, page. 118 - 124, 2012-07-30
- Files in This Item:
- There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.