Microstructure and properties of Mg-3Sn-1Mn (wt%) alloy processed by a novel continuous shearing and rolling and heat treatment SCIE SCOPUS

Title
Microstructure and properties of Mg-3Sn-1Mn (wt%) alloy processed by a novel continuous shearing and rolling and heat treatment
Authors
Guan, RGZhao, ZYZhang, HCui, TLee, CS
Date Issued
2013-01-01
Publisher
ELSEVIER SCIENCE SA
Abstract
A novel semisolid continuous shearing and rolling process for producing Mg-3Sn-1Mn (wt%) alloy strip was proposed, microstructure and properties of Mg-3Sn-1Mn (wt%) alloy strip processed by the proposed process and heat treatment was investigated. For each condition, at least three tensile tests were performed. Under strong cooling and shearing actions caused by the rotating roll and the fixed shoe, eruptive nucleation, direct globular grain growth and dendrite arm breakage took place in the roll-shoe gap, which causes the formation of fine spherical or rosette primary grains. When the casting temperature was 690 degrees C, and the roll speed was 0.052 m s(-1). Mg-3Sn-1Mn (wt%) alloy strip was produced. The microstructures of the strip are mainly composed of fine spherical or rosette grains. After deep rolling, the grains of the strip were elongated, the textures were formed in the deep-rolled strip. The ultimate tensile strength (UTS) of the deep-rolled strip is 276 +/- 3 MPa, and the elongation (EL) is 6.3 +/- 0.1% in the rolling direction (RD). After solution treatment at 480 degrees C for 13 h and aging at 300 degrees C for 12 h, the Mg2Sn phase distributes homogeneously in matrix microstructure and strengthens the mechanical properties, the UTS and EL of the deep-rolled strip reach 305 +/- 3.3 MPa and 7.8 +/- 0.12% in the RD. (C) 2012 Elsevier B.V. All rights reserved.
Keywords
Mg-3Sn-1Mn magnesium alloy; Continuous shearing and rolling; Heat treatment; Microstructure; Property; MECHANICAL-PROPERTIES; ALUMINUM-ALLOY; EXTRUSION PROCESS; MG ALLOY; TEMPERATURE; EVOLUTION; STATE
URI
https://oasis.postech.ac.kr/handle/2014.oak/14676
DOI
10.1016/J.MSEA.2012.08.079
ISSN
0921-5093
Article Type
Article
Citation
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, vol. 559, page. 194 - 200, 2013-01-01
Files in This Item:
There are no files associated with this item.

qr_code

  • mendeley

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

Related Researcher

Researcher

이종수LEE, CHONG SOO
Ferrous & Energy Materials Technology
Read more

Views & Downloads

Browse