- Title
- Optical and field emission properties of thin single-crystalline GaN nanowires
- Authors
- Ha, B; Seo, SH; Cho, JH; Yoon, CS; Yoo, J; Yi, GC; Park, CY; Lee, CJ
- Date Issued
- 2005-06-09
- Publisher
- AMER CHEMICAL SOC
- Abstract
- Thin high-quality gallium nitride (GaN) nanowires were synthesized by a catalytic chemical vapor deposition method. The synthesized GaN nanowires with hexagonal single-crystalline structure had thin diameters of 10-50 nm and lengths of tens of micrometers. The thin GaN nanowires revealed UV bands at 3.481 and 3.285 eV in low-temperature PL measurements due to the recombination of donor-bound excitons and donor-acceptor pairs, respectively. The blue shifts of UV bands in the low-temperature PL measurement were observed, indicating quantum confinement effects in the thin GaN nanowires which have smaller diameters than the exciton Bohr radius, 11 nm. For field emission properties of GaN nanowires, the turn-on field of GaN nanowires was 8.5 V/mu m and the current density was about 0.2 mA/cm(2) at 17.5 V/mu m, which is sufficient for the applications of field emission displays and vacuum microelectronic devices. Moreover, the GaN nanowires indicated stronger emission stability compared with carbon nanotubes.
- Keywords
- GALLIUM NITRIDE NANOWIRES; CHEMICAL-VAPOR-DEPOSITION; PHASE EPITAXY; NANOCRYSTALLINE GAN; CATALYTIC SYNTHESIS; OXIDE NANOWIRES; LOW-TEMPERATURE; FILMS; PHOTOLUMINESCENCE; GROWTH
- URI
- https://oasis.postech.ac.kr/handle/2014.oak/24569
- DOI
- 10.1021/JP044334C
- ISSN
- 1520-6106
- Article Type
- Article
- Citation
- JOURNAL OF PHYSICAL CHEMISTRY B, vol. 109, no. 22, page. 11095 - 11099, 2005-06-09
- Files in This Item:
- There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.