KINETICS AND MECHANISMS FOR NITRIDATION OF FLOATING ALUMINUM POWDER SCIE SCOPUS

Title
KINETICS AND MECHANISMS FOR NITRIDATION OF FLOATING ALUMINUM POWDER
Authors
CHANG, AJRHEE, SWBAIK, SG
Date Issued
1995-01
Publisher
AMER CERAMIC SOC 735 CERAMIC PLACE
Abstract
Aluminum powder entrained by ammonia-containing nitrogen gas was reacted at various temperatures and time to form aluminum nitride powder. The kinetics of nitride formation were determined by a quantitative X-ray analysis and compared with those determined by a nitrogen analysis of-the product. The conversion to aluminum nitride increased with the reaction time following a sigmoidal rate law. The reaction time for full conversion decreased as the temperature increased in the range 1050 degrees-1300 degrees C. The reaction rate constant at a given temperature was evaluated using the Avrami equation. The activation energy for the reaction was 1054 +/- 91 kJ/mol in the temperature range of 1050 degrees-1200 degrees C, and decreased to 322 +/- 70 kJ/mol above 1200 degrees C. Comparative analysis of powders formed below and above 1200 degrees C suggested strongly that the rate-controlling step changed from chemical reaction to mass transport above 1200 degrees C.
URI
https://oasis.postech.ac.kr/handle/2014.oak/29324
DOI
10.1111/j.1151-2916.1995.tb08357.x
ISSN
0002-7820
Article Type
Article
Citation
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, vol. 78, no. 1, page. 33 - 40, 1995-01
Files in This Item:
There are no files associated with this item.

qr_code

  • mendeley

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

Views & Downloads

Browse