Dissolution rate of Al2O3 into molten CaO-SiO2-Al2O3 slags SCIE SCOPUS

Title
Dissolution rate of Al2O3 into molten CaO-SiO2-Al2O3 slags
Authors
Choi, JYLee, HGKim, JS
Date Issued
2002-01
Publisher
IRON STEEL INST JAPAN KEIDANREN KAIKA
Abstract
The dissolution rate of Al2O3 into the CaO-SiO2-Al2O3 slag system was investigated at 1873 K by employing a novel experimental method which involved continual measurement of the torque variation on a rotating alumina rod dipped into a molten slag. Measured torque variation was successfully related to the dissolution rate of the rod. The dissolution rate of alumina was found affected by a number of factors: the rate increased with increasing temperature, the rotating speed of the rod, the CaO content in the slag, and the Al2O3 content in the slag for a fixed CaO content. It was found that the dissolution rate was highly dependent on the viscosity and the diffusivity of slags. The activation energy obtained from an Arrhenius type analysis was in the range of 84 kJ mol(-1). It was concluded that the dissolution of Al2O3 into the CaO-SiO2-Al2O3 slag system was controlled by the mass transfer in the slag phase. An iso-dissolution rate diagram was constructed for the dissolution of Al2O3 into the CaO-SiO2-Al2O3 slag system at 1873 K.
Keywords
dissolution; rate; alumina; Al2O3; CaO-SiO2-Al2O3; slag; ALUMINA-SILICA MELTS; SAPPHIRE; KINETICS
URI
https://oasis.postech.ac.kr/handle/2014.oak/20961
DOI
10.2355/isijinternational.42.852
ISSN
0915-1559
Article Type
Article
Citation
ISIJ INTERNATIONAL, vol. 42, no. 8, page. 852 - 860, 2002-01
Files in This Item:
There are no files associated with this item.

qr_code

  • mendeley

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

Views & Downloads

Browse